6AL-4V Titanium Description: 6AL-4V is the most common alloy of Titanium. ... 6AL-4V offers good weldability. Overall, 6AL-4V exhibits high strength, light weight, and corrosion resistance, which make it an excellent choice for applications in aerospace, medical, oil and gas, marine, and recreational industries.
What is the hardest grade of titanium?
Grade 4
What is the hardness for titanium?
Property Value
---------------- ----------------------
Specific gravity 4.5
Hardness 70 to 74 HRB
Tensile strength 240 MPa (35 ksi) min
Young's modulus 120 GPa (17 × 106 psi)
The price of commercially pure titanium (CP) has risen sharply since 2003 to 2014, from $15.00 per lb to $30.00 per lb. It is an extremely light weight and high strength material.
What is the rate of titanium?
Titanium Grade 1 Price (per kg) Origin Price in INR (per kg)
------------------------------- -------- ---------------------
India Indian Rs.1422
Japan Japanese Rs.1777
UK / Europe Japanese Rs.1990
USA USA Rs.2061
How much is titanium worth in 2021?
The prices of titanium scrap jumped in 2021 due to a drop in global stocks of shavings, a byproduct of aircraft manufacturing. According to IndexBox estimates, the average import price for titanium scrap increased from $2.9 per kg in January 2021 to $4.1 in April 2021.Aug 12, 2021
What is TI-6AL-4V used for?
7.6. Ti–6Al–4V is an alloy that has been widely used in the aerospace industry in compressor blades and casings due to its high specific strength to weight ratio.
Price for Ti-6Al-4V bar(ASTM B348 Gr. 5, annealed): USD21. 20 per kg.
How strong is 6AL 4V titanium?
0 1
------------------------- ------------
Hardness Brinell 334
Hardness Rockwell C 36
Ultimate Tensile Strength 131000 psi
Yield Strength 120000 psi
Machinability Rating 22% of B 112
How do you heat treat 6al4v titanium?
The STOA cycle for Ti-6Al-4V, for example, is heat one hour at 955°C (1750°F), water quench, hold two hours at 705°C (1300°F), and air cool. In this case, STOA improves notch strength and fracture toughness, and provides a creep strength similar to that obtained by regular annealing.
How do you heat treat titanium?
There are three principal types of heat treatment. Stress Relieving Titanium alloys can be stress relieved without adversely affecting strength or ductility. The process for forgings takes place at 595 to 705°C (1100 to 1300°F) for a period of one to two hours, followed by air cooling.
How do you temper titanium?
Set the furnace temperature to the correct specifications: 1,800 to 1850 degrees Fahrenheit if titanium part is alpha alloy; 1,750 to 1,775 degrees if alloy is alpha-beta alloy; and 1,425 to 1,475 degrees if the alloy is beta alloy.